POP multifilament for technical applications

Title Alternative:POP multifilament for technical applications
Simple item page
dc.contributor.advisorKřemenáková, Dana
dc.contributor.authorMncube, Blessing Thokazani
dc.date2010
dc.date.accessioned2013-12-27
dc.date.available2013-12-27
dc.date.committed2010-05-17
dc.date.defense2010-06-01
dc.date.issued2010
dc.date.submitted2009-10-30
dc.degree.levelmgr
dc.descriptionkatedra: KTT; přílohy: 1 CD; rozsah: 112 s.cs
dc.description.abstractMonofilaments are used in the membrane Lamination process. Here in this report, 56 dtex of polypropylene multifilament yarn with 16 fibrous was evaluated for technical application (membrane lamination). Strength of fibers and fibrous bundles were very important parameters especially for industrial applications. This project describes the bundle strength of POP multifilament?s form statistical point of view. Bundles 1 to 10 filaments were tested. Yarns were twisted at 400t/m, 440t/m, 800z/m and 1200t/m count. Two type of twisting technologies were used, and those technologies were ply twister and ring spinning. Based on the information provided by the Company initiated this project. And the results obtain during experiment. It were concluded that 1200t/m was the optimum yarn for a membrane lamination process. Ring spinning technology was recommended technology for twisting the yarn. The best operation condition for POP multifilament concluded was less the 120°C.cs
dc.description.abstractMonofilaments are used in the membrane Lamination process. Here in this report, 56 dtex of polypropylene multifilament yarn with 16 fibrous was evaluated for technical application (membrane lamination). Strength of fibers and fibrous bundles were very important parameters especially for industrial applications. This project describes the bundle strength of POP multifilament?s form statistical point of view. Bundles 1 to 10 filaments were tested. Yarns were twisted at 400t/m, 440t/m, 800z/m and 1200t/m count. Two type of twisting technologies were used, and those technologies were ply twister and ring spinning. Based on the information provided by the Company initiated this project. And the results obtain during experiment. It were concluded that 1200t/m was the optimum yarn for a membrane lamination process. Ring spinning technology was recommended technology for twisting the yarn. The best operation condition for POP multifilament concluded was less the 120°C.en
dc.formattext
dc.identifier.urihttps://dspace.tul.cz/handle/15240/4302
dc.language.isoen
dc.publisherTechnická Univerzita v Libercics
dc.subjectpop multifilamentcs
dc.subjectfibercs
dc.subjectlaminationcs
dc.subjectply twistercs
dc.subjectring spinningcs
dc.subjectpop multifilamenten
dc.subjectfiberen
dc.subjectlaminationen
dc.subjectply twisteren
dc.subjectring spinningen
dc.subject.verbistextilní technologiecs
dc.titlePOP multifilament for technical applicationscs
dc.title.alternativePOP multifilament for technical applicationsen
dc.typeThesis
local.departmentKTTcs
local.facultyFakulta textilnícs
local.identifier.stag18338
local.identifier.verbis439065
local.note.administratorsoprava_A
local.verbis.aktualizace2019-10-05 06:01:18cs
local.verbis.studijniprogramKTT Textilní inženýrství/Textile engineeringcs
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
mgr_18338.pdf
Size:
24.71 MB
Format:
Adobe Portable Document Format
Description:
kvalifikační práce
Download
Collections
Fakulta textilní