Recyklovaná uhlíková vlákna
Title Alternative:Recycled Carbon Fibers
dc.contributor.advisor | Kovačič, Vladimír | |
dc.contributor.author | Forštová, Zuzana | |
dc.date | 2008 | |
dc.date.accessioned | 2014-01-10 | |
dc.date.available | 2014-01-10 | |
dc.date.committed | 2008-05-12 | |
dc.date.defense | 2008-06-10 | |
dc.date.issued | 2008 | |
dc.date.submitted | 2007-10-31 | |
dc.degree.level | mgr | |
dc.description | katedra: KTM; přílohy: 1 CD; rozsah: 97 s., 75 s. příloh | cs |
dc.description.abstract | Diplomová práce zkoumá parametry recyklovaných uhlíkových vláknen z textilních kompozitů. Zabývá se vlastnostmi uhlíkových vláken před a po tepelné pyrolýze. Tyto vlastnosti byly zjišťovány z pěti vzorků uhlíkovo-skelné tkaninové výztuže. Původní nerecyklovaný vzorek pod označením C Virgin slouží pro výrobu kompozitních desek uhlík-epoxid. Zbývající čtyři vzorky vznikly po tepelné pyrolýze kompozitní desky uhlík-epoxid. Pyrolýza byla provedena za určité teploty po určitou dobu. Z toho vzniklo označení vzorků. C 550 N2 znamená, že byl vorek recyklovaný při 550°C v dusíkové atmosféře. Vzorky C 550 vzduch, C 600, C 650 byly recyklované při teplotě 550°C, 600°C, 650°C na vzduchu. Od těchto skutečností se odvíjí vlastnosti uhlíkových vláken a vznikají mezi nimi určité rozdíly. Proto bylo na vláknech provedeno hned několik pokusů. Byl zjišťován průměr jednotlivých vláken d [{$\mu$}m], škodlivost úlomků prachových částic, měrná hmotnost {$\varrho$} [kg/m3], hmotnostní úbytky, jemnost T[tex]. U svazků vláken byla změřena jejich pevnost v tahu {$\sigma$} [MPa], tažnost [%] a modul pružnosti E [GPa]. Jak moc působí pracovní teplota a doba teplené pyrolýzy na jednotlivá vlákna je doloženo fotografiemi z elektronového rastrovacího mikroskopu. | cs |
dc.description.abstract | This diploma thesis examine parameter the Recycled Carbon Fibres of Textile Composite. It is focused on carbon fibres properties before and after a thermal pyrolysis. These properties of carbon fibres have been found out from five samples of carbon-glass textural armature. The first sample is an original unrecycled sample known as C Virgin and it serves for production of carbon-epoxide composite panels. The other four samples have been caused by thermal pyrolysis of carbon-epoxide composite panel. This pyrolysis have been realised during specific and defined time and temperature. From this process the four mentioned samples have come into being. A sample C 550 N2 means that this sample was recycled at the temperature 550°C in nitrogenous atmosphere. The samples C 550, C 600, C 650 were recycled at the temperature 550°C, 600°C and 650°C on air. Carbon fibres properties are unwinded from this realistic facts and from this research were found out visibled differences between mentioned samples. It was realized a number of test on these samples. There were found out a diameter of fibres d [{$\mu$}m], powdery fragments harmfulness, density of fibros {$\varrho$} [kg/m3], their weight-shortages and finesess T [tex] of samples. From fibre-bundles were measured their tensile strenght {$\sigma$} [MPa], elongation to break [%] and modulus of elasticity E [GPa]. Documented photos from electron scanning microscope evidence how to influence temperature and the time of thermal pyrolysis the recycled carbon fibres of textile composite. | en |
dc.format | text | |
dc.identifier.uri | https://dspace.tul.cz/handle/15240/6650 | |
dc.language.iso | cs | |
dc.publisher | Technická Univerzita v Liberci | cs |
dc.subject | uhlíkové vlákno | cs |
dc.subject | recyklované uhlíkové vlákno | cs |
dc.subject | textilní kompozit | cs |
dc.subject | průměr vlákna | cs |
dc.subject | pevnost vlákna | cs |
dc.subject | rizikový faktor | cs |
dc.subject | měrný povrch vlákna | cs |
dc.subject | škodlivost prachových úlomků | cs |
dc.subject | aspektní poměr | cs |
dc.subject | tepelná pyrolýza | cs |
dc.subject | carbon fibre | en |
dc.subject | recycled carbon fibre | en |
dc.subject | textile composite | en |
dc.subject | fibre diameter | en |
dc.subject | fibre tenacity | en |
dc.subject | hazard factor | en |
dc.subject | fiber density | en |
dc.subject | powdery fragments harmfulness | en |
dc.subject | aspect ratio | en |
dc.subject | thermal pyrolysis | en |
dc.subject.verbis | textile materials | en |
dc.title | Recyklovaná uhlíková vlákna | cs |
dc.title.alternative | Recycled Carbon Fibers | en |
dc.type | Thesis | |
local.department | KTM | cs |
local.faculty | Fakulta textilní | cs |
local.identifier.stag | 15425 | |
local.identifier.verbis | 363710 | |
local.note.administrators | oprava_A | |
local.verbis.aktualizace | 2019-10-05 06:12:24 | cs |
local.verbis.studijniprogram | KTM | cs |
Files
Original bundle
1 - 1 of 1
Loading...
- Name:
- mgr_15425.pdf
- Size:
- 35.34 MB
- Format:
- Adobe Portable Document Format
- Description:
- kvalifikační práce