Influence of dopants and preparation method on the thermoluminescence properties of corundum crystals

Date
1980
Journal Title
Journal ISSN
Volume Title
Publisher
Vch Publishers Inc
Abstract
Thermoluminescence (TL) of several types of corundum crystals is described. Undoped crystals showed a weak TL at 15 and 110°C with emission at 330 and 495 nm. Good TL response at 275°C is shown by Cr doped (0.03 wt%) crystals grown by Verneuil method in the oxygen cone of the flame annealed in hydrogen at 1500–1800°C. The most intensive TL response is shown by crystals doped with Ti and Mo (∼ 10−3wt.%) grown by Czochralski method in reducing conditions. The former may be used to the detection of γ-rays dose ≥ 10−3 − 10−2 Gy, the latter ≥ 10−7 − 10−6 Gy. Die Thermolumineszenz (TL) von Korund-Einkristallen wird im Hinblick auf die Präparationsmethode und Dotierung beschrieben. Die undotierten Kristalle zeigten eine relative schwache TL bei 15 und 110°C (λ = 330 und 495 nm). Die nach der Verneuil-Methode gezüchteten und im Wasserstoff getemperten Rubin-Kristalle (0,03 Gew.% Cr) zeigten eine erhöhte TL bei 275°C (λ = 695 nm). Eine ausgeprägte Intensität der Thermolumineszenz (160°C, λ = 420 nm) zeigten die mit Ti und Mo dotierten (∼ 10−3Gew.%) Kristalle, welche nach der Czochralski-Methode in reduzierender Atmosphäre gezüchtet wurden. Der beschriebene Rubin ermöglichtes, die Dosis von γ-Strahlen ≥ 10−3 – 10−2 Gy und beim letztgenannten Material ≥ 10−7 – 10−6 Gy zu messen.
Description
Subject(s)
Citation
ISSN
0023-4753
ISBN
Collections